CHARACTERISTICS
I. Cold rolled products made of low carbon non-alloyed structural steel are used for the production of flat or cold-formed structural elements. Their application is determined by the minimum value of the yield point, or by the tensile strength.
II. Cold rolled products made of fine-grained, atmospheric corrosion
resistant structural steel are mostly used in the building industry and for various constructions. Improved resistance is due to the surface layer of oxides of alloying elements.
Grades according to DIN 1623:2009 |
Heat analysis in % | |||||
---|---|---|---|---|---|---|
CMAX | MnMAX | SiMAX | PMAX | SMAX | NMAX | |
KOSIL 200 S | 0,16 | 0,60 | 0,030 | 0,025 | 0,020 | - |
S215G | 0,18 | 1,50 | - | 0,030 | 0,025 | 0,0105 |
KOSIL 215 S | 0,16 | 0,80 | 0,030 | 0,025 | 0,020 | - |
S245G | 0,20 | 1,60 | - | 0,030 | 0,025 | - |
S325G | 0,20 | 1,60 | 0,55 | 0,030 | 0,025 | - |
Grades according to TN USSK 10025-5:2016 |
Heat analysis in % | ||||||||
---|---|---|---|---|---|---|---|---|---|
CMAX | Mn | Si | P | SMAX | AlMIN | Cu | NiMAX | Cr | |
KONOX 315CR | 0,12 | 0,20 - 0,55 | 0,25 - 0,55 | 0,07 - 0,15 | 0,015 | 0,02 | 0,25 - 0,60 | 0,65 | 0,50 - 1,20 |
Grades according to |
Rp0,2 MIN [MPa] |
Rm [MPa] |
AMIN (%) Lo = 80 mm |
Angle of bend 180° 1) |
---|---|---|---|---|
KOSIL 200 S | 200 | 310 - 430 | 22 | 0,5.a |
S215G | 215 | 360 - 510 | 20 | - |
KOSIL 215 S | 215 | 360 - 470 | 20 | 0,5.a |
S245G | 245 | 430 - 580 | 18 | - |
S325G | 325 | 510 - 680 | 16 | - |
Grades according to TN USSK 10025-5:2016 |
Rp0,2 MIN [MPa] |
Rm [MPa] |
AMIN(%) L0=80 mm |
Bend test | |
---|---|---|---|---|---|
α | D | ||||
KONOX 315CR | 315 | 450 | 23 | 180° | 0,5a |
for KOSIL 200 S, KOSIL 215 S, S215G and corresponding
Nominal thickness [mm] | Width [mm] | |||||
---|---|---|---|---|---|---|
750 | 1105 | 1265 | 1425 | 1500 | ||
0,400 - 0,449 | ||||||
0,450 - 0,749 | ||||||
0,750 - 1,149 | ||||||
1,150 - 2,000 |
for S245 G, S325 G, KONOX 315CR and corresponding
Nominal thickness [mm] | Width [mm] | |||||||
---|---|---|---|---|---|---|---|---|
750 | 1015 | 1085 | 1200 | 1275 | 1325 | |||
0,550 - 0,649 | ||||||||
0,650 - 0,949 | ||||||||
0,950 - 1,249 | ||||||||
1,250 - 1,749 | ||||||||
1,750 - 2,000 |
The width of 700 - 749 mm at the thickness of 0,80 - 2,00 mm is the subject to prior agreement
Thickness [mm] | Length [mm] |
---|---|
0,40 - 1,00 | 1 000 - 3 000 |
1,01 - 2,00 | 1 000 - 3 000 |
NOTE: above 3000mm we produce in cooperation
Thickness | Inner diameter | Outer diameter | Coil | Slit coil | ||
---|---|---|---|---|---|---|
Width | Weight | Width | Weight | |||
0,40 - 1,30 | approx. 500 or 600 | max. 1 800 | 750 - 1 050 | 3 - 15 kg.mm-1 of width | 21 - 600 | max. 15 000 kg |
0,40 - 2,00 | approx. 600 | 750 - 1 500 | 2 - 17 kg.mm-1 of width | 21 - 600 | max. 15 000 kg |
NOTE: thickness is graded by 0,01 mm.
Re < 260 MPa
Nominal thickness | Normal tolerances at width | Reduced tolerances at width | ||
---|---|---|---|---|
≤ 1 200 | > 1200 ≤ 1 500 | ≤ 1 200 | > 1200 ≤ 1 500 | |
> 0,40 ≤ 0,60 | ± 0,03 | ± 0,04 | ± 0,025 | ± 0,030 |
> 0,60 ≤ 0,80 | ± 0,04 | ± 0,05 | ± 0,030 | ± 0,035 |
> 0.80 ≤ 1,00 | ± 0,05 | ± 0,06 | ± 0,035 | ± 0,040 |
> 1,00 ≤ 1,20 | ± 0,06 | ± 0,07 | ± 0,040 | ± 0,050 |
> 1,20 ≤ 1,60 | ± 0,08 | ± 0,09 | ± 0,050 | ± 0,060 |
> 1,60 ≤ 2,00 | ± 0,10 | ± 0,11 | ± 0,060 | ± 0,070 |
NOTE: reduced tolerances are subject to prior agreement
260 < Re < 340 MPa
Nominal thickness | Normal tolerances at width | Reduced tolerances at width | ||
---|---|---|---|---|
≤ 1 200 | > 1200 ≤ 1 500 | ≤ 1 200 | > 1200 ≤ 1 500 | |
> 0,40 ≤ 0,60 | ± 0,04 | ± 0,05 | ± 0,030 | ± 0,035 |
> 0,60 ≤ 0,80 | ± 0,05 | ± 0,06 | ± 0,035 | ± 0,040 |
> 0.80 ≤ 1,00 | ± 0,06 | ± 0,07 | ± 0,040 | ± 0,050 |
> 1,00 ≤ 1,20 | ± 0,07 | ± 0,08 | ± 0,050 | ± 0,060 |
> 1,20 ≤ 1,60 | ± 0,09 | ± 0,11 | ± 0,060 | ± 0,070 |
> 1,60 ≤ 2,00 | ± 0,12 | ± 0,13 | ± 0,070 | ± 0,080 |
NOTE: reduced tolerances are subject to prior agreement
Re < 260 MPa
Nominal width | Normal tolerances at thickness | Reduced tolerances1) at thickness | ||||
---|---|---|---|---|---|---|
< 0,70 | ≥ 0,70 < 1,20 | ≥ 1,20 | < 0,70 | ≥ 0,70 < 1,20 | ≥ 1,20 | |
> 600 < 1 200 | 10 | 8 | 7 | 5 | 4 | 3 |
≥ 1 200 < 1 500 | 12 | 10 | 8 | 6 | 5 | 4 |
≥ 1 500 | 17 | 15 | 13 | 8 | 7 | 6 |
1) reduced tolerances are subject to prior agreement
260 ≤ Re < 340 MPa
Nominal width | Normal tolerances at thickness | Reduced tolerances1) at thickness | ||||
---|---|---|---|---|---|---|
< 0,70 | ≥ 0,70 < 1,20 | ≥ 1,20 | < 0,70 | ≥ 0,70 < 1,20 | ≥ 1,20 | |
> 600 < 1 200 | 13 | 10 | 8 | 8 | 6 | 5 |
≥ 1 200 < 1 500 | 15 | 13 | 11 | 9 | 8 | 6 |
≥ 1 500 | 20 | 19 | 17 | 12 | 10 | 9 |
1) reduced tolerances are subject to prior agreement